Abstract: Cast Mg-6 wt pct Al alloy solution-treated at 683 K for 16 h and aged at 498 K was coated by plasma electrolytic oxidation (PEO) method. The Mg-6 wt pct Al alloy aged for 16 h exhibited the highest microhardness and wear resistance. After PEO coating, however, the microhardness and wear resistance of coatings on Mg-6 wt pct Al alloy showed a tendency to decrease with increasing aging time, which was in aggrement with the change of thickness with aging time. In addition, the coatings on solution-treated Mg-6 wt pct Al alloy had better microhardness and wear resistance than those on aged Mg-6 wt pct Al alloys. Consequently, it can be understood that the aging treatment has a deleterious influence on the mechanical properties of coatings on Mg-6 wt pct Al alloy.

Key words: Cast Mg-6 wt pct Al, Aging treatment, Plasma electrolytic oxidation...