Effect of Pressure and Temperature in phase transformation and properties of Ti aluminide obtained through reaction synthesis

J. Mater. Sci. Technol. ›› 2010, Vol. 26 ›› Issue (8): 693-704.

• Research Articles • 上一篇下一篇

Effect of Pressure and Temperature in phase transformation and properties of Ti aluminide obtained through reaction synthesis

R.K.Gupta,Bhanu Pant

Vikram Sarabhai Space Centre, ISRO, Trivandrum – 695 022

收稿日期:2008-07-17 出版日期:2010-08-28 发布日期:2010-08-23
通讯作者: R.K.Gupta

Effect of Pressure and Temperature on Phase Transformation and Properties of Titanium Aluminide Obtained through Reaction Synthesis

R.K. Gupta, Bhanu Pant, Vijaya Agarwala, R.C. Agarwala, P.P. Sinha

1) Vikram Sarabhai Space Centre, ISRO, Trivandrum{695 022, India
2) Indian Institute of Technology, Roorkee, Roorkee{247 667, India

Received:2008-07-17 Online:2010-08-28 Published:2010-08-23
Contact: R.K. Gupta

摘要/Abstract

关键词: Titanium aluminides, Reaction synthesis, Reaction synthesis, Phase transformation

Abstract:

Reaction synthesis process has been used to develop γ titanium aluminide using elemental powders. Powder mixture of Ti-48 at. pct Al was prepared in ball mill and reaction synthesis was carried out in hot press with varying temperature and pressure. Titanium aluminide synthesized under high pressure and temperature resulted in better properties with respect to densification, homogenization response, mechanical properties and oxidation resistance as compared to that synthesized under low pressure and temperature. Al rich phases were observed in as-synthesized condition in all the experiments. However, some Ti rich phases were also found in high pressure-temperature synthesized samples. Density, hardness and tensile strength have been correlated with applied pressure through empirical relations. Variation in density with pressure is found to be logarithmic whereas hardness and tensile strength variation with pressure is polynomial.

Key words: Titanium aluminide, Reaction synthesis, Phase transformation

R.K.Gupta Bhanu Pant. Effect of Pressure and Temperature in phase transformation and properties of Ti aluminide obtained through reaction synthesis[J]. J. Mater. Sci. Technol., 2010, 26(8): 693-704.

R.K. Gupta Bhanu Pant Vijaya Agarwala R.C. Agarwala P.P. Sinha. Effect of Pressure and Temperature on Phase Transformation and Properties of Titanium Aluminide Obtained through Reaction Synthesis[J]. J Mater Sci Technol, 2010, 26(8): 693-704.

参考文献

[1 ] U.R. Kattener, J.C. Lin and Y.A.Chang: Metall. Mater. Trans. A, 1992, 23, 2081. [2 ] H.A. Lipsitt: Titanium Aluminides|An Overview, in Proc. of High Temp Ordered Intermetallic Alloys, eds. C.C. Koch, C.T. Liu, N.S. Stollo®, 1985, 351. [3 ] Y. Mutoh, T. Moriya1, S.J. Zhu and Y. Mizuhara: Small Fatigue Crack Behavior in °-base Tial Intermetallics, in The 3rd Paci¯c Rim Int Conference on Advanced Materials and Processing, Honolulu, Hawaii, 1998, 12. [4 ] Y.W. Kim and D.M. Dimiduk: JOM, 1991, 43, 40. [5 ] S.C. Huang and E.L. Hall: Acta Metall. Mater., 1991, 6, 1053. [6 ] T. Tetsui: Intermetallics, 2002, 10, 239. [7 ] M. Yamaguchi: Mater. Sci. Technol., 1992, 8, 299. [8 ] M. Yamaguchi, H. Inui and K. Ito: Acta Mater., 2000, 48, 307. [9 ] D.K. Peacock: Met. Mater., 1989, 5, 474. [10] R.M. Imayev, V.M. Imayev and G. Salischev: Scripta Metall. Mater., 1993, 29, 713. [11] R.M. Imayev, V.M. Imayev, G. Salischev: Scripta Metall. Mater., 1993, 29, 719. [12] G. Salischev, R.M. Imayev, O.N. Senkov, V.M. Imayev, N.K. Gabdullin, M.R. Shagiev, A.V. Kuznestov and F.H. Froes: Mater. Sci. Eng. A, 2000, 286, 236. [13] M.R. Shagiev, G. Salischev, R.M. Imayev, V.M. Imayev and A.V. Kuznestov: Mater. Sci. Forum, 2004, 447-448, 317. [14] B. Dogan, R. Wagner and P.A. Beaven: Scripta Metall. Mater., 1991, 25, 773. [15] M. Dahms, J. Seeger, W. Smarsly and B. Wildhagen: ISIJ Int., 1991, 31, 1093. [16] A.P. Savstkii: Powder Metall. Met. Ceram., 1980, 19, 488. [17] A.P. Savstkii and N.N. Burtsev: Powder Metall. Met. Ceram., 1981, 20, 681. [18] N. Bertolino, M. Monagheddu, A. Tacca, P. Giuliani, C. Zanotti, U. Tamburini Anselmi: Intermetallics, 2003, 11, 41. [19] D.J. Lee and D.N. Yoon: Powder Mater. Int., 1988, 20, 15. [20] A. Bose, B.H. Rabin and R.M. German: Powder Mater. Int., 1988, 20, 25. [21] C. Nishimura and C.T. Liu: Acta Metall. Mater., 1993, 41, 113. [22] J.T. Guo and C.Y. Cui: Key Eng. Mater., 2002, 217, 117. [23] Z.B. Ge, K.X. Chen, J.M. Guo, H.P. Zhou and M.F. Jose Ferreira: J. Eur. Ceram. Soc., 2003, 23, 567. [24] B.H. Rabin and R.N. Wright: Metall. Mater. Trans. A, 1991, 22, 277. [25] S. Gedevanishvili and S.C. Deevi: Mater. Sci. Eng. A, 2002, 325, 163. [26] R.M. German: Liquid Phase Sintering, Plenum Press, New York, 1985, 1. [27] W.D. Kingery, J.M. Woulbourn and F.R. Charvat: J. Am. Ceram. Soc., 1963, 46, 391. [28] Y.V. Naidich, I.A. Lavrinenko and V.A. Evdokimov: Powder Metall. Met. Ceram., 1974, 13, 26. [29] J.D. Whittenberger: Solid State Processing for high Temperature Alloys and Composites, in Proc. of Solid State Powder Processing, The Minerals, Metals and Mater Society, eds. A.H. Clauer and J.J. Barbadillo, 1990, 137. [30] H.C. Yi and J.J. Moore: Scripta Metall., 1988, 22, 1889. [31] J.C. Rawers and W.R.Wrzesinki: J. Mater. Sci., 1992, 27, 2877. [32] J.K. Kim, T.K. Kin, T.K. Lee, S.K. Hwang, S.W. Nam and N.J. Kim: Improvement of Metallurgical Processing Parameters for EPM TiAl-1.4Mn-2Mn-2Mo Alloy, in Proc. on Gamma Ti Aluminides, eds. Y.W. Kim, D.M. Dimiduk and M.H. Loretto, The Minerals Metals and Material Society, 1999, 231. [33] R.M. German, A. Bose and N.S. Stolloff: in Proc on High Temp Ordered Intermetallic Alloys III, eds. C.T. Liu, A.I. Taub, N.S. Stolo® and C.C. Koch, 1989, 133, 403. [34] A.R.C. Westwood: Metall. Mater. Trans. A, 1988, 19, 749. [35] B.J. Lee and N. Saunders: Z. Metallkd, 1997, 88, 152. [36] B. Pant, V. Agarwala, R.C. Agarwala and P.P. Sinha: Trans. Indian Inst. Met., 2007, 60, 925. [37] X. Wang, H.Y. Sohn and M.E. Schlesinger: Mater. Sci. Eng. A, 1994, 186, 151. [38] M. Sujata, S. Bhargava and S. Sangal: J. Mater. Sci. Lett., 1997, 16, 1175. [39] B.D. Cullity: Elements of X-Ray Di®raction, 3rd edn, Addison-Wiley Publishing Company, Inc., USA, 2001. [40] R.R. Oddone and R.M. German: Adv. Powder Metall., 1989, 3, 475. [41] T. Kawabata, T. Tamura and O. Izumi: Parameters for Ductility Improvement in TiAl, in Proc. on High Temp Ordered Intermetallic Alloys III, eds. C.T. Liu, A.I. Taub, N.S. Stoloff and C.C. Koch, 1989, 329. [42] S.C. Huang and P.A. Siemers: Metall. Mater. Trans. A, 1989, 20, 1899. [43] S.L. Semiatin and P.A. Mcquay: Metall. Mater. Trans. A, 1992, 23, 149. [44] Y.D. Hahn and Y.T. Lee: Advances in Powder Metallurgy & Particulate Materials, Vol. 9, eds. J.M. Capus and R.M. German, Metal Powder Industries Federation, Princeton, New Jersey, 1992, 309. [45] I.A. Ibrahim, F.A. Mohammed and E.J. Lavernia: J. Mater. Sci., 1991, 26, 1137. [46] S. Srinivasan, P.B. Desch and R.B. Schwartz: Scripta Metall. Mater., 1991, 25, 2513. [47] T. Christman and M. Jain: Scripta Metall. Mater., 1991, 25, 767. [48] G.X. Wang and M. Dahms: Scripta Metall. Mater., 1992, 26, 717. [49] S. Hamada, H. Hamada, H. Suzuki and A.J. Nozue: J. Mater. Sci., 2002, 37, 1107. [50] Y. Nishiyama, T. Miyashita, S. Isobe and T. Noda: Development of Titanium Aluminide Turbocharger Rotors, in Proc. on High Temp Aluminides and Intermetallics, eds. S.H. Whang, C.T. Liu, D.P. Pope and J.O. Steigler, The Minerals Metals and Mater So- ciety, USA, 1990, 557. [51] K. Furuya and J. Moteff: Metall. Mater. Trans. A, 1981, 12, 1303. [52] T.S. Srivatsan, W.O. Soboyejo and M. Strangwood: Eng. Fracture Mech., 199, 52, 107. [53] M.R.Yang and S.K. Wu: Bull. College Eng. NTU, 2003, 89, 3.

Effect of Pressure and Temperature in phase transformation and properties of Ti aluminide obtained through reaction synthesis

Effect of Pressure and Temperature on Phase Transformation and Properties of Titanium Aluminide Obtained through Reaction Synthesis

RichHTML

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 1

编辑推荐

Metrics

本文评价