Segregation Behaviour and Microstructure of Alloy 718VADER Ingot

Yueguang YU; Jie FU and Xishan XIE(University of Science and Technology Bejing, Beijing, 100083, China)Jialong XU and Chunyong JING(Shanghai Iron and Steel Research Institute, Shanghai, 200940, China)   

  • 收稿日期:1994-11-28 修回日期:1994-11-28 出版日期:1994-11-28 发布日期:2009-10-10

Segregation Behaviour and Microstructure of Alloy 718VADER Ingot

Yueguang YU; Jie FU and Xishan XIE(University of Science and Technology Bejing, Beijing, 100083, China)Jialong XU and Chunyong JING(Shanghai Iron and Steel Research Institute, Shanghai, 200940, China)   

  • Received:1994-11-28 Revised:1994-11-28 Online:1994-11-28 Published:2009-10-10

RichHTML

0

PDF (PC)

1072

摘要： l.lntroductionTheVADER(VacuumArcDoubleElectrodeRemelting)processisanewmeltingandcastingtechnologyintroducedbySpecialMetalsCorpora-tiontenyearsago[l-3].Inthisnewprocess,twoopposingandconsumableelectrodesareusedin-steadofoneintheVARprocess(seeFig.l).TheVADERandVARprocessesbothutilizeconsumab1eelectrodearcremelting,buttheyareverydifferentintermsofelectroderemeltingandingotsolidificationcharacter....

Abstract: The segregation behaviour and miclostructure of an alloy 718 VADER ingot in comparison with a VAR ingot were studied. The results show that one serious problem of the alloy 718 VADER ingot is dealing with radial chemistry gradients (especially macro-segregation in Nb). The main factor of Nb gradient forming is the flow of Nb rich fluid through passages among the cellular structures driven by centrifugal force from the rotating mold, Detailed structure and micro-segregation studies on ingots impress us that the VADER process does not show the advantage on the improvement of micro-segregation especially in Nb. The cellular structure produced by the VADER process is no more effective in reducjng Nb micro-segregation during homogenization treatment than the dendritic structure by the VAR process. Experimental results lead us to believe that the VADER process is unsuitable to manufacture alloy 718.