Wear-resisting Oxide Films for 900℃

M.B.Peterson(Wear Sciences Corporation, Arnold, Maryland, USA)Shizhuo LI(Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110015, China)S.F.Murray(Rensselaer Polytechnic Institute, Thoy, New York, USA)   

  • 收稿日期:1997-03-28 修回日期:1997-03-28 出版日期:1997-03-28 发布日期:2009-10-10

Wear-resisting Oxide Films for 900℃

M.B.Peterson(Wear Sciences Corporation, Arnold, Maryland, USA)Shizhuo LI(Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110015, China)S.F.Murray(Rensselaer Polytechnic Institute, Thoy, New York, USA)   

  • Received:1997-03-28 Revised:1997-03-28 Online:1997-03-28 Published:2009-10-10

RichHTML

1

PDF (PC)

710

摘要： 1.IntroductionForthepast50years,temperaturesinadvancedheatengineshavebeenincreasing.Newgenerationengineswillrequirelubricantsfor1O00"Candhigher.0neofthemostcriticalapplicationsistheregeneratorsealsontheautom0tivegasturbine.0tliercriticalapplicationsincludecagesforceramicrollillg-contactbearings,controlsurfacesforadvancedjetenginesandvariable-areanozzlesf0rturboramjetpropulsi0nsys-temswhichope....

Abstract: A study was conducted to develop low-friction, wear-resistant surfaces on high temperature alloys for the temperature range from 26℃ to 900℃. The approach investigated consists of modifying the naturally occurring oxide film in order to improve its tribological properties. Improvement is needed at low temperatures where the oxide film, previously formed at high temperature, spalls due to stresses induced by sliding. Experiments with Ti, W and Ta additions show a beneficial effect when added to Ni and Ni-base alloys. Low friction can be maintained down to 100℃ from 900℃. For unalloyed Ni friction and surface damage increases at 400℃ to 500℃. Two new alloys were perpared based on the beneficial results of binary alloys and ZrO2 diffusion in Ni.Low friction at temperature above 500℃ and reasonable values (0.32~0.42) at low temperature are obtained.