Information and Service
|
|
| This Article | |
 |
Supporting info |
|
PDF(436KB) |
|
[HTML] |
|
Reference |
| Service and feedback | |
|
Add to Citation Manager |
|
Cite This Article |
|
Email Alert |
| Keywords | |
|
Potassium hexatitanate |
|
X-ray diffraction |
|
HRTEM technique |
|
Crystal structure |
| Authors | |
|
Bingshe XU |
|
Peide HAN |
|
Jian LIANG |
|
Yuan YU |
|
Huiqiang BAO |
|
Xuguang LIU |
| PubMed | |
|
Article by |
|
Article by |
|
Article by |
|
Article by |
|
Article by |
|
Article by |
A HRTEM and XRD Study of the Potassium Hexatitanate Nanowires
Bingshe XU, Peide HAN, Jian LIANG, Yuan YU, Huiqiang BAO, Xuguang LIU
College of Materials Science and Engineering, Taiyuan University of Technology, Taiyuan 030024, China...
The structure of potassium hexatitanate (K¬¬2T¬6O¬13) nanowires has been investigated using both the Rietveld powder diffraction profile fitting technique and high resolution transmission electron microscopy (HRTEM) image simulations. From the Rietveld analysis it was shown that the nanowires had a monoclinic structure of the space group C2/M and the lattice parameters were a=1.5582 nm, b=0.382 nm, c=0.9112 nm. HRTEM conclusions agree with refinement results obtained from experimental XRD data. The good agreement between the experimental and simulated images confirms that the nanowires is indeed K¬¬2T¬6O¬13 nanowire.The growth axes of nanowires were mainly along the [010] direction.