EFFECIS OF TEMPERATURE AND OVERLOAD RETARDATION ON CORROSION FATIGUE CRACK GROWTH OF HIGH STRENGTH STEEL

Abstract

Abstract: The fatigue crack growth rate (CGR) of ultra high strength steel 30CrMnSiNi2A in distilled water at 18,35 and 55℃ were measured.It was confirmed that the temperature is strongly af- fected on the corrosion fatigue CGR of ultra high strength steel.An expression concerning the effects of Δ K and temperature on the CGR was proposed.The fact that the apparent activation energy (36.6 kJ/mol) resulted from regressive analysis of CGR data was similar to the activation energy of hydrogen diffusion in γ-Fe,strongly supporting the theory of hydrogen-assisted crack growth.The overload retardation effect was greatly reduced in cor- rosion fatigue crack growth,especially at lower frequency,e.g.,0.1 Hz.This phenomenon might be due to the increase of the SCC component of CGR after an overload.

Key words: corrosion fatigue, crack growth rate, temperature effect, overload retardation effect

QIAN Yourong HE Xiangdong Beijing University of Aeronautics and Astronautics,Beijing,China QIAN Yourong,Dept.of Materials Science and Engineering,Beijing University of Aeronautics and Astronautics,Beijing 100083,China. EFFECIS OF TEMPERATURE AND OVERLOAD RETARDATION ON CORROSION FATIGUE CRACK GROWTH OF HIGH STRENGTH STEEL[J]. Acta Metallurgica Sinica (English Letters), 1990, 3(3): 204-207.

[1]	Xue Han, Dan Zhang, Song Zhang, Mohammed R. I. Abueida, Lili Tan, Xiaopeng Lu, Qiang Wang, Huanye Liu. Fatigue and Corrosion Fatigue Properties of Mg-Zn-Zr-Nd Alloys in Glucose-Containing Simulated Body Fluids [J]. Acta Metallurgica Sinica (English Letters), 2024, 37(9): 1533-1550.
[2]	A. Ullah, A. Khan, Z.B. Bao, Y.F. Yang, M.M. Xu, S.L. Zhu, F.H. Wang. Temperature Effect on Early Oxidation Behavior of NiCoCrAlY Coatings: Microstructure and Phase Transformation [J]. Acta Metallurgica Sinica (English Letters), 2022, 35(6): 975-984.
[3]	Yu-Lin Cheng, Xiao-Jiao Zuo, Xiao-Guang Yuan, Hong-Jun Huang, Yi-Fan Zhang. Influence of DC Current on Corrosion Behaviour of Copper-Aluminium Composite Plates [J]. Acta Metallurgica Sinica (English Letters), 2021, 34(8): 1142-1152.
[4]	Jiaqi Hu, Qite Li, Hong Gao. Influence of Twinning Texture on the Corrosion Fatigue Behavior of Extruded Magnesium Alloys [J]. Acta Metallurgica Sinica (English Letters), 2021, 34(1): 65-76.
[5]	Yan Liu, Jun Zhang, Shu-Jun Li, Wen-Tao Hou, Hao Wang, Qin-Si Xu, Yu-Lin Hao, Rui Yang. Effect of HIP Treatment on Fatigue Crack Growth Behavior of Ti-6Al-4V Alloy Fabricated by Electron Beam Melting [J]. Acta Metallurgica Sinica (English Letters), 2017, 30(12): 1163-1168.
[6]	Zuo-Yan Ye, Dao-Xin Liu, Xiao-Hua Zhang, Xiao-Ming Zhang, Ming-Xia Lei, Zhi Yang. Corrosion Fatigue Behavior of 7A85 Aluminum Alloy Thick Plate in NaCl Solution [J]. Acta Metallurgica Sinica (English Letters), 2015, 28(8): 1047-1054.
[7]	Amir SULTAN, Riffat Asim PASHA,Mifrah ALI, Muhammad Zubair KHAN, Muhammad Afzal KHAN, Naeem Ullah DAR,Masood SHAH. Numerical Simulation and Experimental Veri?cation of CMOD in SENT Specimen: Application on FCGR of Welded Tool Steel [J]. Acta Metallurgica Sinica (English Letters), 2013, 26(1): 92-96.
[8]	Fang WANG,Weicheng CUI. Effect of three dimensional stress state on unstable fracture condition and crack opening level in a new crack growth model [J]. Acta Metallurgica Sinica (English Letters), 2010, 23(1): 41-49.
[9]	J.X.Dong, M.C.Zhang, Y.P.Zeng, X.S.Xie. CREEP CRACK GROWTH BEHAVIOR OF ALLOY 718 DURING HIGH TEMPERATURE EXPOSURE [J]. Acta Metallurgica Sinica (English Letters), 2005, 18(2): 164-172 .
[10]	W.C.Cui, X.P.Huang. A GENERAL CONSTITUTIVE RELATION FOR FATIGUE CRACK GROWTH ANALYSIS OF METAL STRUCTURES [J]. Acta Metallurgica Sinica (English Letters), 2003, 16(5): 342-354 .
[11]	B.F. Ding, Y.S. Wu, S.H. Abubakir. CORROSION FATIGUE BEHAVIOR OF STAINLESS STEEL 3RE60 IN 3.5% SODIUM CHLORIDE SOLUTION [J]. Acta Metallurgica Sinica (English Letters), 2002, 15(6): 538-544 .
[12]	X.S.Wang, S.Q.Zhu. A NOVEL PARAMETER FOR EVALUATING THE FATIGUE CRACK GROWTH RATE IN CARBON STEELS [J]. Acta Metallurgica Sinica (English Letters), 2001, 14(4): 271-279 .
[13]	Author H.F. Huang and S.L. Liu Laboratory of Material Mechanical Properties, Beijing Institute of Aeronautical Materials (BIAM), Beijing 100095, China Manuscript received 18 October 1998. CRACK GROWTH BEHAVIOR IN TITANIUM ALLOY TC11AT ROOM AND HIGH TEMPERATURES [J]. Acta Metallurgica Sinica (English Letters), 1999, 12(1): 80-84.
[14]	Q. Gao; Y.X. Zhao and L.X. Cai (Institute of Applied Mechanics, Southwest Jiaotong University, Chengdu 610031, China). A PROBABILISTIC ASSESSMENT OF TEMPERATURE EFFECTS ON THE LOW CYCLE FATIGUE BEHAVIOUR OF 1Cr_(18)Ni_9Ti STEEL WELD METAL [J]. Acta Metallurgica Sinica (English Letters), 1998, 11(6): 477-484.
[15]	J.H. Xie; Y.S. Wu; J.Q. He; X.Z.Yang and R.Z. Zhu (Department of Surface Science & Corrosion Engineering, University of Science and Technology Beijing,Beijing 100083, China). CORROSION FATIGUE CRACK INITIATION BEHAVIOR OF 316L STAINLESS STEEL IN HANK'S SOLUTION [J]. Acta Metallurgica Sinica (English Letters), 1996, 9(5): 333-337.

EFFECIS OF TEMPERATURE AND OVERLOAD RETARDATION ON CORROSION FATIGUE CRACK GROWTH OF HIGH STRENGTH STEEL

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments