EFFECT OF POTENTIAL ON INTERACTION BETWEEN STRESS CORROSION CRACKING AND CORROSION FATIGUE OF AUSTENITIC STAINLESS STEEL IN BOILING 42% MgCl_2 SOLUTION

Abstract

Abstract: The environment-sensitive fracture behaviour of 0Cr18Ni9Ti austenitic stainless steel in boiling 42% MgCl_2 under the specific load of low frequency and high mean stress was inves- tigated from the relations and differences of crack growth rates and fractographs between stress corrosion fatigue and stress corrosion cracking.The interaction between stress corro- sion cracking and corrosion fatigue was also studied from fracture characteristics with empha- sis on the effects of applied potential on the interaction.

Key words: environment-sensitive fracture, stress corrosion cracking, corrosion fatigue, stress corrosion fatigue

FENG Tao CHEN Liangshi KE Wei Corrosion Science Laboratory,Institute of Corrosion and Protection of Metals,Academia Sinica,Shenyang,China. EFFECT OF POTENTIAL ON INTERACTION BETWEEN STRESS CORROSION CRACKING AND CORROSION FATIGUE OF AUSTENITIC STAINLESS STEEL IN BOILING 42% MgCl_2 SOLUTION[J]. Acta Metallurgica Sinica (English Letters), 1991, 4(9): 168-173.

[1]	Xue Han, Dan Zhang, Song Zhang, Mohammed R. I. Abueida, Lili Tan, Xiaopeng Lu, Qiang Wang, Huanye Liu. Fatigue and Corrosion Fatigue Properties of Mg-Zn-Zr-Nd Alloys in Glucose-Containing Simulated Body Fluids [J]. Acta Metallurgica Sinica (English Letters), 2024, 37(9): 1533-1550.
[2]	Wen Wang, Shan-Yong Chen, Ke Qiao, Pai Peng, Peng Han, Bing Wu, Chen-Xi Wang, Jia Wang, Yu-Hao Wang, Kuai-She Wang. Microstructure, Mechanical Properties, and Corrosion Behavior of Mg-Al-Ca Alloy Prepared by Friction Stir Processing [J]. Acta Metallurgica Sinica (English Letters), 2022, 35(5): 703-713.
[3]	F. Shi, L. Yan, J. Hu, L. F. Wang, T. Z. Li, W. Li, X. J. Guan, C. M. Liu, X. W. Li. Improving Intergranular Stress Corrosion Cracking Resistance in a Fe-18Cr-17Mn-2Mo-0.85N Austenitic Stainless Steel Through Grain Boundary Character Distribution Optimization [J]. Acta Metallurgica Sinica (English Letters), 2022, 35(11): 1849-1861.
[4]	Hongchi Ma, Baijie Zhao, Yi Fan, Kui Xiao, Jinbin Zhao, Xuequn Cheng, Xiaogang Li. Simultaneously Improving Mechanical Properties and Stress Corrosion Cracking Resistance of High-Strength Low-Alloy Steel via Finish Rolling within Non-recrystallization Temperature [J]. Acta Metallurgica Sinica (English Letters), 2021, 34(4): 565-578.
[5]	Ji-Jin Xu, Shuai Wang, Ze Chai, Chun Yu, Jun-Mei Chen, Hao Lu. Comparison of the Stress Corrosion Cracking Behaviour of AISI 304 Pipes Welded by TIG and LBW [J]. Acta Metallurgica Sinica (English Letters), 2021, 34(4): 579-589.
[6]	Jiaqi Hu, Qite Li, Hong Gao. Influence of Twinning Texture on the Corrosion Fatigue Behavior of Extruded Magnesium Alloys [J]. Acta Metallurgica Sinica (English Letters), 2021, 34(1): 65-76.
[7]	Zhixiong Zhu, Xingxu Jiang, Gang Wei, Xiaogang Fang, Zhihong Zhong, Kuijing Song, Jian Han, Zhengyi Jiang. Influence of Zn Content on Microstructures, Mechanical Properties and Stress Corrosion Behavior of AA5083 Aluminum Alloy [J]. Acta Metallurgica Sinica (English Letters), 2020, 33(10): 1369-1378.
[8]	Jin-Jin Zhao, Xian-Bin Liu, Shuai Hu, En-Hou Han. Effect of Cl^- Concentration on the SCC Behavior of 13Cr Stainless Steel in High-Pressure CO₂ Environment [J]. Acta Metallurgica Sinica (English Letters), 2019, 32(12): 1459-1469.
[9]	Hong-Liang Ming,Zhi-Ming Zhang,Peng-Yuan Xiu,Jian-Qiu Wang,En-Hou Han,Wei Ke,Ming-Xing Su. Microstructure, Residual Strain and Stress Corrosion Cracking Behavior in 316L Heat-Affected Zone [J]. Acta Metallurgica Sinica (English Letters), 2016, 29(9): 848-858.
[10]	Jian Chen, Jian-Qiu Wang, En-Hou Han, Wei Ke, D. W. Shoesmith. Effect of Hydrogen on Corrosion and Stress Corrosion Cracking of AZ91 Alloy in Aqueous Solutions [J]. Acta Metallurgica Sinica (English Letters), 2016, 29(1): 1-7.
[11]	Zuo-Yan Ye, Dao-Xin Liu, Xiao-Hua Zhang, Xiao-Ming Zhang, Ming-Xia Lei, Zhi Yang. Corrosion Fatigue Behavior of 7A85 Aluminum Alloy Thick Plate in NaCl Solution [J]. Acta Metallurgica Sinica (English Letters), 2015, 28(8): 1047-1054.
[12]	Zhiyong LIU, Cuiwei DU, Xin ZHANG, Fuming WANG,Xiaogang LI. Effect of pH Value on Stress Corrosion Cracking of X70 Pipeline Steel in Acidic Soil Environment [J]. Acta Metallurgica Sinica (English Letters), 2013, 26(4): 489-496.
[13]	J.X. Pan, K.Y. Kim. THE EFFECT OF W ON THE REPASSIVATION BEHAVIOR OF Ni-ADDED STAINLESS STEELS [J]. Acta Metallurgica Sinica (English Letters), 2005, 18(4): 489-496 .
[14]	B.F. Ding, Y.S. Wu, S.H. Abubakir. CORROSION FATIGUE BEHAVIOR OF STAINLESS STEEL 3RE60 IN 3.5% SODIUM CHLORIDE SOLUTION [J]. Acta Metallurgica Sinica (English Letters), 2002, 15(6): 538-544 .
[15]	S.Q. Li; J.I. Dickson and J.P. Bailon (Central Iron and Steel Research Institute (CISRI), Beijing 100081, China)(Ecole Polytecnique de Montreal, Montreal H3C 3A7, Canada). STUDY ON FRACTOGRAPHY OF TRANSGRANULAR SCC OF 70Cu-3OZn IN AN AMMONIACAL SOLUTION [J]. Acta Metallurgica Sinica (English Letters), 1998, 11(5): 347-357.

EFFECT OF POTENTIAL ON INTERACTION BETWEEN STRESS CORROSION CRACKING AND CORROSION FATIGUE OF AUSTENITIC STAINLESS STEEL IN BOILING 42% MgCl_2 SOLUTION

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments