J. Mater. Sci. Technol. ›› 2019, Vol. 35 ›› Issue (10): 2263-2268.DOI: 10.1016/j.jmst.2019.05.042
• Orginal Article • Previous Articles Next Articles
Received:
2019-05-08
Revised:
2019-05-15
Accepted:
2019-05-20
Online:
2019-10-05
Published:
2019-08-28
Contact:
Sui Manling
Bo Zhou, Manling Sui. High density stacking faults of {10$\bar{1}$1} compression twin in magnesium alloys[J]. J. Mater. Sci. Technol., 2019, 35(10): 2263-2268.
Fig. 1. (a) TEM micrograph of a {10$\bar{1}$1} twin. (b) Schematic illustration of {10$\bar{1}$1} twin in a HCP unit cell. (c) Enlarged micrograph of the twin tip marked in (a). (d) SAED pattern corresponding to the {10$\bar{1}$1} twin along [$\bar{1}$2$\bar{1}$0] zone axis, yellow arrows indicate the SFs on (0001)T plane and (e) enlarged micrograph of the front part of the twin marked in (a). The green, red, and yellow lines represent the CTBs, steps and SFs, respectively.
Fig. 2. (a, b) HRTEM images of {10$\bar{1}$1} twin tip. (c, d) Enlarged HRTEM images of Step A and Step B, respectively. The dashed yellow lines represent the boundaries and the white arrow shows the SF in the twin. The insets of atomic planes schematically show the stacking sequence of the close-packed planes, in which the yellow, blue, and green balls represent the layer-A, layer-B, and layer-C, respectively. The red vector circuits are drawn surrounding Step A and Step B, and the direction vector of each circuit segment along the [1$\bar{2}$10] projection is accordingly listed the built-in tables, in which Λ= $ (2/3)^ \frac{1}{2}$c/a, P is the transformation matrix from the coordinate frame of the twin (marked by a subscript T) to that of the matrix (marked by a subscript M). (e, f) εyy strain maps of Step A and Step B. (g) Strain distribution curves of the lines 1-3 marked in (e) and (f).
Fig. 3. (a, b) The atomic marked HRTEM image and corresponding simulation diagram of Step A. The dashed circles and dashed red lines represent the ideal position of the atoms and the (0001)M planes, respectively. The inset shows the difference of the atomic arrangement and lattice spacing in the (0001)M and ({10$\bar{11}$})T planes. (c, d) The atomic marked HRTEM image and corresponding simulation diagram of Step B. The yellow, blue, and green balls represent the atoms on layer A, B, and C, respectively. The inset shows the two-layer FCC stacking sequence.
Fig. 4. (a, b) Schematic illustration of the high density SFs expanding with the {10$\bar{1}$1} twin thickening. (c, d) HRTEM images of the PSFs terminated at the bottom TBs of the {10$\bar{1}$1} twins.
|
[1] | Qiyu Liao, Yanchao Jiang, Qichi Le, Xingrui Chen, Chunlong Cheng, Ke Hu, Dandan Li. Hot deformation behavior and processing map development of AZ110 alloy with and without addition of La-rich Mish Metal [J]. J. Mater. Sci. Technol., 2021, 61(0): 1-15. |
[2] | Qianqian Jin, Xiaohong Shao, Shijian Zheng, Yangtao Zhou, Bo Zhang, Xiuliang Ma. Interfacial dislocations dominated lateral growth of long-period stacking ordered phase in Mg alloys [J]. J. Mater. Sci. Technol., 2021, 61(0): 114-118. |
[3] | Dan Zhang, Qi Han, Kun Yu, Xiaopeng Lu, Ying Liu, Ze Lu, Qiang Wang. Antibacterial activities against Porphyromonas gingivalis and biological characteristics of copper-bearing PEO coatings on magnesium [J]. J. Mater. Sci. Technol., 2021, 61(0): 33-45. |
[4] | B.N. Du, Z.Y. Hu, L.Y. Sheng, D.K. Xu, Y.X. Qiao, B.J. Wang, J. Wang, Y.F. Zheng, T.F. Xi. Microstructural characteristics and mechanical properties of the hot extruded Mg-Zn-Y-Nd alloys [J]. J. Mater. Sci. Technol., 2021, 60(0): 44-55. |
[5] | S.H. Lu, D. Wu, R.S. Chen, En-hou Han. Microstructure and texture optimization by static recrystallization originating from {10-12} extension twins in a Mg-Gd-Y alloy [J]. J. Mater. Sci. Technol., 2020, 59(0): 44-60. |
[6] | Xiaoxiao Wei, Li Jin, Fenghua Wang, Jing Li, Nan Ye, Zhenyan Zhang, Jie Dong. High strength and ductility Mg-8Gd-3Y-0.5Zr alloy with bimodal structure and nano-precipitates [J]. J. Mater. Sci. Technol., 2020, 44(0): 19-23. |
[7] | Xiao-Yuan Wang, Yu-Fei Wang, Cheng Wang, Shun Xu, Jian Rong, Zhi-Zheng Yang, Jin-Guo Wang, Hui-Yuan Wang. A simultaneous improvement of both strength and ductility by Sn addition in as-extruded Mg-6Al-4Zn alloy [J]. J. Mater. Sci. Technol., 2020, 49(0): 117-125. |
[8] | Zhixin Zhang, Jiangkun Fan, Bin Tang, Hongchao Kou, Jian Wang, Xin Wang, Shiying Wang, Qingjiang Wang, Zhiyong Chen, Jinshan Li. Microstructural evolution and FCC twinning behavior during hot deformation of high temperature titanium alloy Ti65 [J]. J. Mater. Sci. Technol., 2020, 49(0): 56-69. |
[9] | Zhao-Qi Zhang, Rong-Chang Zeng, Cun-Guo Lin, Li Wang, Xiao-Bo Chen, Dong-Chu Chen. Corrosion resistance of self-cleaning silane/polypropylene composite coatings on magnesium alloy AZ31 [J]. J. Mater. Sci. Technol., 2020, 41(0): 43-55. |
[10] | Pengfei Zhang, Yunchang Xin, Ling Zhang, Shiwei Pan, Qing Liu. On the texture memory effect of a cross-rolled Mg-2Zn-2Gd plate after unidirectional rolling [J]. J. Mater. Sci. Technol., 2020, 41(0): 98-104. |
[11] | Bassem Barkia, Pascal Aubry, Paul Haghi-Ashtiani, Thierry Auger, Lionel Gosmain, Frédéric Schuster, Hicham Maskrot. On the origin of the high tensile strength and ductility of additively manufactured 316L stainless steel: Multiscale investigation [J]. J. Mater. Sci. Technol., 2020, 41(0): 209-218. |
[12] | Hui Pan, Liwei Wang, Yi Lin, Feng Ge, Kang Zhao, Xin Wang, Zhongyu Cui. Mechanistic study of ammonium-induced corrosion of AZ31 magnesium alloy in sulfate solution [J]. J. Mater. Sci. Technol., 2020, 54(0): 1-13. |
[13] | Timothy Alexander Listyawan, Hyunjong Lee, Nokeun Park. A new guide for improving mechanical properties of non-equiatomic FeCoCrMnNi medium- and high-entropy alloys with ultrasonic nanocrystal surface modification process [J]. J. Mater. Sci. Technol., 2020, 59(0): 37-43. |
[14] | Hao Li, Qinghui Zeng, Pengfei Yang, Qi Sun, Jianmin Wang, Jian Tu, Minhao Zhu. Towards understanding twinning behavior near fracture surface in magnesium [J]. J. Mater. Sci. Technol., 2020, 43(0): 230-237. |
[15] | Yubing Zhang, Jinglian Du, Kang Wang, Huiyuan Wang, Shu Li, Feng Liu. Application of non-equilibrium dendrite growth model considering thermo-kinetic correlation in twin-roll casting [J]. J. Mater. Sci. Technol., 2020, 44(0): 209-222. |
Viewed | ||||||
Full text |
|
|||||
Abstract |
|
|||||