J Mater Sci Technol ›› 1999, Vol. 15 ›› Issue (05): 486-488.

• Research Articles • Previous Articles    

Fractals in Steel-Aluminum Solid to Liquid Bonding

Peng ZHANG, Yunhui DU, Xueping REN, Limin BA, Hanwu LIU, Jianzhong CUI   

  1. School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China...
  • Received:1998-10-24 Revised:1998-11-30 Online:1999-09-28 Published:2009-10-10
  • Contact: Peng ZHANG

Abstract: This paper studied the fractal characteristic of the interfacial shear surface of steel-Al solid to liquid bonding plate, and determined the relationship between fractal dimension and interfacial shear strength. The research results showed that the relationship between fractal dimension and interfacial shear strength could be described as y=26.2x+4.2 (where y was interfacial shear strength, x was fractal dimension) and when 08Al steel plate was coarsened by steel wire wheel which was made up with steel wires whose diameter were 1.4-1.6 mm, the optimum coarsening pattern of the steel plate surface could be got, the corresponding maximum interfacial shear surface fractal dimension of the bonding plate was 2.33, and the maximum interfacial shear strength of the bonding plate was 65.3 MPa.

Key words: