Corrosion of AISI 4130 Steel Alloy under Hydrodynamic Condition in Ethylene Glycol+ Water+NO2-­­­­ Solution

doi:10.1016/j.jmst.2012.11.013

J. Mater. Sci. Technol. ›› 2013, Vol. 29 ›› Issue (1): 89-96.DOI: 10.1016/j.jmst.2012.11.013

• Reviews • 上一篇

收稿日期:2011-10-01 修回日期:2012-01-26 出版日期:2013-01-30 发布日期:2013-02-04

Corrosion of AISI 4130 Steel Alloy under Hydrodynamic Condition in Ethylene Glycol+ Water+NO₂^-Solution

I. Danaee, M. Niknejad Khomami, A.A. Attar

Abadan Faculty of Petroleum Engineering, Petroleum University of Technology, Abadan, Iran

Received:2011-10-01 Revised:2012-01-26 Online:2013-01-30 Published:2013-02-04
Contact: I. Danaee

摘要/Abstract

Abstract:

The electrochemical behavior of steel alloy in ethylene glycol–water mixture at different solution rotating speeds was investigated by polarization curves and AC impedance measurements (EIS). The results obtained showed that corrosion rate was not changed significantly at different rotating speeds and was decreased with increasing ethylene glycol concentration. The effect of nitrite as an inhibitor was studied and high inhibition efficiency was obtained. It was found that surface passivation occurred in the presence of inhibitor. The inhibiting effect of the nitrite was explained on the basis of the competitive adsorption between the inorganic anions and the aggressive Cl⁻ ions and the adsorption isotherm basically obeys the Flory–Huggins adsorption isotherm. Thermodynamic parameters for steel corrosion and inhibitor adsorption were determined, which revealed that the adsorption process is spontaneous.

Key words: Steel 4130, Ethylene glycol, Corrosion, Hydrodynamic, Nitrite

. [J]. J. Mater. Sci. Technol., 2013, 29(1): 89-96.

I. Danaee, M. Niknejad Khomami, A.A. Attar . Corrosion of AISI 4130 Steel Alloy under Hydrodynamic Condition in Ethylene Glycol+ Water+NO₂^-Solution[J]. J. Mater. Sci. Technol., 2013, 29(1): 89-96.

参考文献

[1] L.Y. Xu, Y.F. Cheng, Corros. Sci. 50 (2008) 2094-3003.

[2] S. Tierce, N. Pébere, C. Blanc, C. Casenave, G. Mankowski,H. Robidou, Corros. Sci. 49 (2007) 4581-4590.

[3] S. Tierce, N. Pébere, C. Blanc, C. Casenave, G. Mankowski,H. Robidou, Electrochim. Acta 52 (2006) 1092-1097.

[4] O.K. Abiola, J.O.E. Otaigbe, Corros. Sci. 50 (2008) 242-249.

[5] G.A. Zhang, L.Y. Xu, Y.F. Cheng, Electrochim. Acta 53 (2008)8245-8252.

[6] A.M. Fekry, M.Z. Fatayerji, Electrochim. Acta 54 (2009) 6522.

[7] Y.S. Choi, J.J. Shim, J.G. Kim, J. Alloy Compd. 391 (2005)162-169.

[8] H. Fang, X. Hui, G. Chen, J. Alloy. Compd. 464 (2008) 292-295.

[9] E. Samiento-Bustos, J.G. González Rodriguez, J. Uruchurtu,G. Dominguez-Patiño, V.M. Salinas-Bravo, Corros. Sci. 50(2008) 2296-2303.

[10] E. Samiento-Bustos, J.G. González-Rodriguez, J. Uruchurtu,V.M. Salinas-Bravo, Corros. Sci. 51 (2009) 1107-1114.

[11] E. Blasco-Tamarit,A. Igual-Muñoz, J.GarcíaAntón,D.García-García,Corros. Sci. 48 (2006) 863-886.

[12] Y.C. Chen, C.M. Lee, S.K. Yen, S.D. Chyou, Corros. Sci. 49 (2007)3917-3925.

[13] A.M. Cabral, W. Trabelsi, R. Serra, M.F. Montemor, M.L.Zheludkevich, M.G.S. Ferreira, Corros. Sci. 48 (2006)3740-3758.

[14] S.S. Abd El Rehima, S.M. Sayyah, M.M. El-Deeb, S.M. Kamal,R.E. Azooz, Mater. Chem. Phys. 123 (2010) 20-27.

[15] A. Igual Muñoz, J. García Antón, S. López Nuévalos, J.L. Guiñón,V. Pérez Herranz, Corros. Sci. 46 (2004) 2955-2974.

[16] K.N. Mohana, A.M. Badiea, Corros. Sci. 50 (2008) 2939-2947.

[17] S.M. Abd El Haleem, S. Abd El Wanees, E.E. Abd El Aal, A. Diab,Corros. Sci. 52 (2010) 292-302.

[18] D. Wang, X. Tang, Y. Qiu, F. Gan, G.Z. Chen, Corros. Sci. 47(2005) 2157-2172.

[19] K. Aramaki, Corros. Sci. 43 (2001) 2201-2215.

[20] H. Wang, R. Akid, Corros. Sci. 50 (2008) 1142-1148.

[21] I. Danaee, S. Noori, Int. J. Hydrogen Energy 36 (2011) 12102-12111.

[22] J.R. Macdonald, Solid State Ionics 13 (1984) 147-149.

[23] I. Danaee, M. Jafarian, F. Forouzandeh, F. Gobal, M.G. Mahjani,J. Phys. Chem. B 112 (2008) 15933-15940.

[24] I. Danaee, J. Electroanal. Chem. 662 (2011) 415-420.

[25] G. Song, D. StJohn, Corros. Sci. 46 (2004) 1381-1399.

[26] M. Jafarian, F. Gobal, I. Danaee, R. Biabani, M.G. Mahjani,Electrochim. Acta 53 (2008) 4528-4536.

[27] M.B. Valcarce, M. Vázquez, Electrochim. Acta 53 (2008) 5007-5015.

[28] A.G. Muñoz, J.W. Schultze, Electrochim. Acta 49 (2004) 293-301.

[29] S.A.M. Refaey, S.S. Abd El-Rehim, F. Taha, M.B. Saleh, R.A.Ahmed, Appl. Surf. Sci. 158 (2000) 190-196.

[30] F. Bentiss, M. Lebrini, M. Lagrenée, Corros. Sci. 47 (2005) 2915-2931.

[31] M.S. Morad, A.M. Kamal El-Dean, Corros. Sci. 48 (2006) 3398-3412.

[32] L. Herrag, B. Hammouti, S. Elkadiri, A. Aouniti, C. Jama,H. Vezin, F. Bentiss, Corros. Sci. 52 (2010) 3042-3051.

[33] A.S. Fouda, A.A. Al-Sarawy, Desalination 201 (2006) 1-13.

[34] T. Szauer, A. Brandt, Electrochim. Acta 26 (1981) 1257-1260.

[35] R. Solmaz, G. Kardas, M. Culha, B. Yaz?c?, M. Erbil, Electrochim.Acta 53 (2008) 5941-5952.

[36] G.N. Mu, X.M. Li, F. Li, Mater. Chem. Phys. 86 (2004) 59-68.

[37] I. Ahamad, R. Prasad, M.A. Quraishi, Corros. Sci. 52 (2010)933-942.

[38] L.M. Vracar, D.M. Drazic, Corros. Sci. 44 (2002) 1669-1680.

[39] S.E. Nataraja, T.V. Venkatesha, K. Manjunatha, B. Poojary,M.K. Pavithra, H.C. Tandon, Corros. Sci. 53 (2011) 2651-2659.

[40] X. Li, G. Mu, Appl. Surf. Sci. 252 (2005) 1254-1265.

[41] J.M. Bastidas, P. Pinilla, E. Cano, J.L. Polo, S. Miguel, Corros. Sci.45 (2003) 427-449.

[42] M. Bouklah, B. Hammouti, M. Lagrenee, F. Bentiss, Corros. Sci.48 (2006) 2831-2842.

[43] M. Bouklah, N. Benchat, B. Hammouti, A. Aouniti, S. Kertit,Mater. Lett. 60 (2006) 1901-1905.

[44] G. Mu, X. Li, G. Liu, Corros. Sci. 47 (2005) 1932-1952.

[45] N.P. Cosman, K. Fatih, S.G. Roscoe, J. Electroanal. Chem. 574(2005) 261-271.

[46] S. Tamil Sevil, V. Raman, N. Rajendran, J. Appl. Electrochem. 33(2003) 1175-1182.

[47] M. Outirite, M. Lagrenee, M. Lebrini, M. Traisnel, C. Jama,H. Vezin, F. Bentiss, Electrochim. Acta 55 (2010) 1670-1681.

Corrosion of AISI 4130 Steel Alloy under Hydrodynamic Condition in Ethylene Glycol+ Water+NO₂^-Solution

RichHTML

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 0

编辑推荐

Metrics

本文评价